In a recent posting the OP asked how to post pictures. In addition to the conventional way of adding photos by uploading an attachment, you can also embed a photo right into the text of a posting using a screen shot of the photo. This works on my Windows 10 desk top computer using an App...

Had to chuckle at this bit of prophetic advice, how true!

I understand about doing what ya can with what ya got, been there done that for a long time. Certainly steps cone speed control has it's place and, in fact, I still use step cones on a couple of machines. But, where I can, I've converted most of the equipment to VFD controls for reasons...

I agree with Chris' recommendation to get a VFD for your grinder. There is nothing more important than controlling tool speed (belts in this case) when metal working. The step cones will offer some speed control, but they won't usually give you the speed that is needed, they are clunky to deal...

The KM18-T is a 120v single thermocouple kiln. The KM18-T Pro is a 240v, 3 thermocouple kiln. I have the Pro version. The TC's are mounted in the top of the chamber and control each of the three heating elements independently. That improves the uniformity of heat throughout the chamber.

While we're talking MagnaCut, what's your preferred HT temps? Cryo, or not? Have you found anything particularly different or difficult in Ht'ing or grinding MagnaCut?

Chris, thank you VERY much for detailing your process. And, the reference to finishing a gun stock is also helpful. It's interesting to note that the guy who wrote the gun stock finishing article speculated that: "I believe that there is a chemical reaction or catalyst occurring between the...

That's a surprise, never would have thought Armor-All would be a good finishing ingredient. Is there something about its UV protection characteristic that adds value? What mixture do you use?

Interesting video from Kyle on this 2 part epoxy. A couple thoughts - when doing a single knife this would be expensive at about $27/can. Once the epoxy is activated in the can it has a 48 hour pot life. Also, I wonder if the material would be prone to chipping or peeling, particularly on...

As I dive deeper into the world of stainless knives with WA handles, I'd like to see if there any ideas about handle finishes. At this point I'm limiting the handle composition to natural, un-stabilized, wood with highlight stacks of contrasting woods and G-10. On oily woods like Bocota and...

Beautiful knife - that sucker will definitely cut a serious amount of pancakes! What a thoughtful photo review of Chris' knife, well done by all.

Do you have examples of these ovens?

If it's not too much trouble, could you give us an overview of how your setup works? Are the molds under pressure or vacuum? Thanks

Opaul... something that caught my eye is the can of Varathane Wood Hardener sitting in the background of this photo. When and how do you use it? BTW - pretty cleaver spring compression setup!

Nice job Ken! It's always fun to build a new tool.

Thanks for the tip, I'm going to start doing that.

Beautiful knife, well done! Oh... and... ah... is that background one of the aprons you wear in the shop? :)

A PID controller should keep the temp +/- a degree or two. You probably want to add Kawool insulation to improve temperature stabilization. Those countertop ovens are often poorly insulated. To attach the PID I mentioned in your previous post, just rip out the wiring to the timer and...

Now there's a nifty idea!

No doubt beating on a blade will change its shape. But cold working steel after heat treating seems like a bad idea Each hammer blow will set up a stress point in the blade that could lead to eventual cracking or potential further warping. Part of the objective of heat treating is to reduce...