Hi Ernie,
Is that the blade you had Clint test? If so, I'm impressed that you were that high in rockwell with the oil you were using; just going off all the time I spent with 1095 and canola oil. To answer your question, I think some would say to just restart your recipe and I think others would say it would be a good idea to do a quick normalizing cycle (probably two times at around 1450 and air cool) beforehand to eliminat any possible warpage.
My suggestion would be to order some faster oil if you are set on using 1095. If not, I would go to another steel (I think you said before that you have used O-1). I am pretty certain with a HT oven and the canola, you will be able to put some knives together. That is what I told myself a while back. Find a steel you are getting good HT results with and go with it. I am not the type of person to use a different steel for every day of the week. It is different when you are doing the HT yourself. I think you'll find yourself devoting a lot of time to "perfecting" a recipe!
Good luck.