Hi Guys,
Have done my research and concluded that these two were the best to choose.
The S7 is more work in the heat treatment stages than H13.
H13 can be hardened to about 52 rc i think.
I am not sure of S7 when the piece is thicker than 2.5" , which all my pieces will be at.
So, which one would you choose for a 40-80 lb piece for a post anvil?
considering both will be sent out to be professionally heat treated.
Double or triple quench ?
thanks,
Jon