MagnaCut heat treat question

[ACLakey]

For those heat treating MagnaCut, what thickness are you taking the bevels to prior to heat treating?

 

[Gene Kimmi]

I’m using 1/8” and under and do all my grinding after heat treat.

 

[MTBob]

While we're talking MagnaCut, what's your preferred HT temps? Cryo, or not?
Have you found anything particularly different or difficult in Ht'ing or grinding MagnaCut?

 

[Taz575]

MagnaCut doesn't seem particularly difficult to grind when hardened. CPM20CV and S90V are a PITA (especially S90V), but Magnacut feels about like CPM154 or S35VN after hardening. A little harder than simple carbons/AEB-L/Nitro V after HT, but nothing horrible/curse worthy!

 

[Edwardshandmadeknives]

While we're talking MagnaCut, what's your preferred HT temps? Cryo, or not?
Have you found anything particularly different or difficult in Ht'ing or grinding MagnaCut?

I just started using it, it seems a lot like CPM154 for grinding. Haven’t tried grinding it hardened yet. I do a little bit of a bevel before HT, probably about .075 or so.