Jim Adams Customs
Well-Known Member
I tried to heat treat couple of CPM154 blades and they only harden to about 41 RC. I could use all the help I can get. What is the best way to heat treat it.
Last edited:
have we had another go at this Jim?
That's strange... Could you check it on a different hardness tester?
-John
Where did you get your steel, Jim?
--nathan
Someone has mixed up some steel along the way. I'm getting ready to do some CPM 154. If you want to send it to me I'll do it with mine and check the hardness to make sure but it appears you guys have already done all that can be done with it. Hopefully you don't have a bunch of that stuff.