Ive been going over crucibles data..It seems there are several different ways to "quench" this steel. Air, positive pressure,salt or even interrupted oil...It looks like a austnizing temp of abut 2100° with a 1000° temper is suppose to yield a 63rc...Has anyone been heat treating this with plates and how did it go with plate quenching..Also did you use sub zero as part of the quench? thanks
CPM10v heat treat ?'s..
- Thread starter Kentucky
- Start date