A small batch to relax me.
I did some Cardo No Kami with copper tube handle. That is the handle making which relaxed me (the hammer help a lot).
4 friction folder, copper handle, stainless handle, XC75 blade , 3mm thick, v flat grind, water differential hardening, 170°c tempering.
Top from bottom
12,5 cm closed, 20 cm long, 7,8 cm sharp, thickness 6mm and 8,5 to the pivot, highness 2,3 cm to the highest
12,6 cm closed, 19,2 cm long, 7,3 cm sharp, thickness 6mm and 8,5 to the pivot, highness 2,3 cm to the highest
12,5 cm closed, 19,2 cm long, 7,3 cm sharp, thickness 6mm et 8,5 to the pivot, highness 2,7 cm to the highest
10 cm closed, 15 cm long, 5,8 cm sharp, thickness 6mm et 8,5 to the pivot, highness 2,7 cm to the highest
Mine on the top after some month of edc . That is less shiny.
I did some Cardo No Kami with copper tube handle. That is the handle making which relaxed me (the hammer help a lot).
4 friction folder, copper handle, stainless handle, XC75 blade , 3mm thick, v flat grind, water differential hardening, 170°c tempering.
Top from bottom
12,5 cm closed, 20 cm long, 7,8 cm sharp, thickness 6mm and 8,5 to the pivot, highness 2,3 cm to the highest
12,6 cm closed, 19,2 cm long, 7,3 cm sharp, thickness 6mm and 8,5 to the pivot, highness 2,3 cm to the highest
12,5 cm closed, 19,2 cm long, 7,3 cm sharp, thickness 6mm et 8,5 to the pivot, highness 2,7 cm to the highest
10 cm closed, 15 cm long, 5,8 cm sharp, thickness 6mm et 8,5 to the pivot, highness 2,7 cm to the highest
Mine on the top after some month of edc . That is less shiny.