I have some 15N20 steel, and am not sure if it would make a good blade, when used by itself, or how to heat treat it, I know it is used in damascus with other steels, but what about just 15N20 by itself? I am wanting to use it for a super thin slicer for my wife. My question is, will 15N20 make a good blade? And if so, would you heat treat it like other 10xx steels or some other method? Any help on temps and soak times and quenchents would be appreciated. Thanks in advance for any help.