Steel is 1084
Oil quench
Handle is Bocote
Pins and lanyard are ss
This blade came from a batch that I did a bend test on. I could get them to finally break at just before right at or just after 45 degrees. Don't get me wrong they did crack around 30 degrees. I was happy with it. i canMt wait to get going again. Oh does anyone have suggestions about the handle shape or is it good?