It is still a little thick so a little more forge time is in order. I am thinking of leaving it forge finished. I did a little bit of grinding to see how it was coming along.
Does if effect the steel if you heat treat over the temp stated in the specs? Say it calls for 1500 before quench and you quench at 1900, will it effect the steel in a negative way?