Search results

Sorry for the late answer. With this wheel I can make a full shallow hollow grind on thin stock-the grind can be without cheating 1 1/4 inch in height at 0.140 inch stock.

Here is my new belt grinder, that my friend made for me. Contact wheel is 20 inch made by Hilzinger Germany.

Thanks. He loved it.

This is a gift for my father 50th birthday. Knife is made from damasteel heimskringla patern at 62-63HRC, with a stonewash anodized ti6al4v liner and clip, and 3d carbon fiber handle. Blade is 4inch long, weight is 125gr. including the silver scull. Thanks for watching.

Thank you. I'm glad you like it.

Thank you Bill for the exceptional tutorial!!! http://knifedogs.com/showthread.php?15590-Texas-Toothpick-Slipjoint-WIP-Tutorial Here is the result-blade is RWL-34 at 62-63HRC(with cryo in LN), spring is 1.4034 steel at 48-49HRC and amboyna handle.

Thanks Randy!

Hi Guys! Here is my latest knife. Blade is 0.150 tick RWL-34, cryo treated 62-63HRC, flat ground to about 0,015 inch Frame is Ti 6al V4 Weight-4.09oz blade length-3,74 inch overall length- 8,66 inch

Hi. Here is my latest knife. Its 9 inch long, RWL-34 steel at 63-64 HRC with extra black canvas micarta. Its inspired from Bob Lum's knife-Stalker.

Here is what I found. http://www.boneclones.com/KO-006S.htm

Thank you. I buy dino bone from here:https://www.brisa.fi/portal/index.php?option=com_oscommerce&osMod=index&cPath=98_60 Its made from natural materials and acrylic resin, its easy to drill, sand and polish, but you have to worked very carefully, because if you apply to much pressure you can...

Thank you fellaws. Buyer really like them.

Steel for this knives is AEB-L at 64-65 HRC, grind is full flat at the one side, and chisel grind at the other, handle is from dinobone, grenadill(African blackwood) and nickel silver. Blades are etch in ferric trichloride. Thanks for looking.

I am quenching the blade in oil without removing the foil. There is no problem with fire ignition if you keep your blade sunk in oil.

Yes. Oil quenching with low viscosity oils will give much higher hardness. SS foil will slow the cooling and you will not experience twisting and warping. Its important first to cool ticker part of the knife and after that the thin.

Tod, I use ss foil for RWL-34 and i heat treated at 1980 for 15 minutes and quench in compressor oil (compAir fluid force or gardner denver aeon 3000) after quenching before tempering hardnes is 68-70HRC and tempering at 345F hardness is 64.5 HRC. Tempering at 400F hardness is 61-62HRC. I hope...

Thanks. When the customer test it, i will post the resultts.

Base model is Spyderco Buchcraft; scandy grind at 12 degrees per side; steel is CPM 3V whit hardness 65-66 HRC (Triple tempering with a holding time of 2 hours at 520 C). Wood for handle is red malee burl whit 8 coats of danish oil and polished whit carnauba wax. Sheath is multipositional wet...

Thanks guys.

My last knives-first is 0.275 thick RWL-34, 62HRC, convex edge, and second is RWL-34 0.200 thick at 62-64 HRC hollow grind.