I have had good results re-heat treating S35VN without any extra cycles required. Having said that, I would note that this steel gets it's edge retention not so much from blade overall hardness as from very hard and wear resistant vanadium and niobium carbides. It doesn't need to be as hard as, for instance, simple carbon steels, to outperform them for wear resistance.
Rob!