Recent content by v-6

  1. v-6

    to hard

    Guys, i'am tried of my sheaths being hard after i dye them. pray tell me how to get them soft again. thank vern
  2. v-6

    to hard

    Guys, i'am tried of my sheaths being hard after i dye them. pray tell me how to get them soft again. thank vern :biggrin:
  3. v-6

    handle material

    does anyone know where i can buy Orange Zombie Skull Handle , or the Green material. does any one know what this material is? thanks vern
  4. v-6

    g10

    Guys this was the first time using g10. well i need help , how do you make g10 shine ,i see a lot of them that shine . so lets see what I'm missing. so help me if you will. thanks vern :o:o:o
  5. v-6

    epoxy

    Just used up the last tube of epoxy and wanted to see which epoxy most people use? vern ps : please tell me why i get all these add when i post.
  6. v-6

    30, water jet knifes

    Im needey , i had a guy give me 30 blank out of a 1930's saw blade. i can not ask him if he had it tested or not. so i need to know if someone out there that can test one to let me what kind it is. we can talk money when we fined someone. maybe someone knows someone. thanks vern v-6:les:
  7. v-6

    utube

    thanks guys now i know. beings i did not have any teaching only this fourm and i thought i missed something. thanks guys vern
  8. v-6

    utube

    After watching Nick Wheeler on sanding , I have a ? . What is the grease he's talking about. I sent him a email but he has to be to busy to take time to look at his email. If i was as good as he is it would be a long time before i could get to my email. thanks vern :les:
  9. v-6

    1095 Quench

    you mmite see if your getting down below 900 in the right amount of time.
  10. v-6

    plasma cam

    about $7000
  11. v-6

    plasma cam

    this is what i,m talking about. http://www.plasmacam.com/indexfla.php v-6
  12. v-6

    plasma cam

    Has any one got to use a plasma cam for cutting your blanks and guards. if so how did you do? My buddy has one to be here this coming month , cant wait to see how he does. vern
  13. v-6

    ? hamon

    i tryed a hamom with a wird side. one side of my 1095 turned out good and the other side did about 1/3 of the other . what did i do wrong? i don't think the clay was to thick, but maybe it was. thanks vern
  14. v-6

    After not doing it for a year ,i could use a little help

    Been off do to stroke and need a little help. I heat-treated 4 blades of 1095 , cleaned them up and started to sand them down for a saten look. sanded to 400 grit by hand (for med reason) and i see a gost of carbon in the blade , so i did it again,and again,and again. it still there, so how...
  15. v-6

    divit

    yep, and another one about 3" vern