I have read where the forging requires multiple quench cycles but haven't read anywhere about the need for the multiple quenches for stock removal. No doubt that's because before now 52100 HAD to be forged. But thanks to Aldo, that's not true any more.
Suppose I got some thin 52100 from Aldo that was already the thickness I needed and only needed to profile and grind to shape... How would the heat treat be different from if I were to forge it?